Research from the European Space Agency has helped to develop an aircraft-grade titanium-aluminum alloy that's half the weight of conventional nickel superalloys but has similar properties. This alloy could make jet turbine blades (such as this one shown in flight) 45 percent lighter. (Source: Creative Commons–A. Rueda)
The cost of titanium isn't as astronomical as it used to be, based on information I've heard from several manufacturers that make fasteners, engine parts, and other components for the aerospace industry. Prices have been declining for a decade or so, as new sources have become available. Combining it with aluminum, as in this alloy, has helped to bring that cost down even more.
@Ann: Thanks for posting this. Metals and metalcasting are two of my favorite topics.
Nickel aluminide has been around for decades, but it is difficult to cast, so it is only in the past few years that it has started to be taken seriously as an alternative to superalloys in turbine applications. General Electric uses investment-cast nickel aluminide for the low-pressure turbine blades in its GEnx engines, and also uses a nickel-aluminide coating on the high-pressure turbine blades. NASA did a lot of work to support this.
It will be interesting to see whether casting in this type of centrifuge is a practical manufacturing method.
Interesting article but there are some practical realities to overcome.
There are three types of blades in a modern gas turbine engine--fan, compressor, and turbine. The fan blades form the large fan at the front of the engine that essentially acts like a propeller (or bird shredder) and operates at low temperatures. FAA engine certification rules designate the fan blade a critical part as failure can result in conditions hazardous to continued flight.
Compressor and turbine blades are not considered critical in this respect as the thinking is even if a failure occurs and the engine is shut down as a result, the fragments exit the tailpipe with no hazard to continued safe flight of the aircraft. One may argue that an engine shutdown is unsafe although the aircraft is certified to fly on one engine. Blades are extremely high integrity parts.
Maybe this is a leap in metallurgical technology however we are a long way from replacing reliable and durable single crystal nickel superalloys with any titanium alloy in the hot section of gas turbine engines. Current designs are running turbine inlet gas temperatures above the melting point of the nickel blade and vane materials--cooling is key here and this design requirement demands internally cooled blade and vane castings that are difficult to produce.
The cold (compressor) section may be more suitable for the material although again current designs are pushing temperatures at the compressor exit above 1200F. For fan blades applications, integrity will have to be demonstrated rigorously. Composites are currently used in this application with great success to reduce weight.
Also any practical use must consider the fabrication cost of the material which appears astronomical.
Design collaboration now includes the entire value chain. From suppliers to customers, purchasing to outside experts, the collaborative design team includes internal and external groups. The design process now stretches across the globe in multiple software formats.
A new high-pressure injection-molding technology produces near-net shape parts with 2-inch-thick walls from high-performance materials like PEEK, PAI, and carbon-filled polymers. Parts show no voids, sinks, or porosity, have more consistent mechanical properties, and are stronger.
Focus on Fundamentals consists of 45-minute on-line classes that cover a host of technologies. You learn without leaving the comfort of your desk. All classes are taught by subject-matter experts and all are archived. So if you can't attend live, attend at your convenience.