Several considerations must be weighed during these conversions. Plastikos began its evaluation with prints of the part and two options: a single piece with molded threads, or a two-piece molded assembly.
Analysis revealed that the single-piece option with molded-in threads would need a tougher, stronger, more costly material to prevent the threads from tearing during the core-pull process. It would also mean a more complex, higher-risk tool design, which might cause difficulty during molding in filling out the threads with the stronger resin material. Instead, Plastikos recommended installing a separate threaded component after molding the part, for a relatively low cost and little complexity.
This option allowed the customer to use a more familiar material and a simpler mold design.
This example underlines the importance of engaging the mold making, molding, and material supply people, as well as the parts designer, up front, said Katen. “It’s best to get in with the customer early on, even when they’re at the paper napkin sketch stage. Several customers will say I have an idea -- is this feasible? What would you need to make it more feasible?”
For example, Micro Mold recommends part designers use consistent thicknesses wherever possible. A lot of thick-to-thin changes can cause problems in manufacturing, such as trouble filling out thicker walled areas.
The example also illustrates some of the controversy surrounding whether integrating multiple steps within a single molded part is always a good idea. There can be design engineering and design limitations to consider when incorporating more features into a tool, said Myers. “The industry has been seeing more multi-shot applications. But is the facility set up for it? Is the product’s application geared toward it?”
Reducing or eliminating post-processing handling does lead to reduced labor costs, said Clinton McDade, senior designer of plastic products for Schaefer Systems International. A single part from the machine that’s ready to package may look like the ideal solution from this perspective. “But to make this part in one piece, sometimes complexity must be added into the mold, such as moving slides to avoid die-lock,” he said. “This can lead to increased mold cost, longer part cycle times, and more downtime for mold maintenance, all directly affecting speed and cost. This one-part product may also require a higher tonnage machine, with its higher overhead rate.”
The two pieces of a two-part product can be made in less expensive, open/shut molds that run on smaller machines with lower overhead rates. On the other hand, manufacturing this final product requires two machines and two cycle times, in addition to the time required for handling and assembly.
“Regardless of how you juggle the manufacturing variables, the ultimate result must be a part that meets the customer’s functional needs,” said McDade. A two-piece product may make the most sense from the standpoint of manufacturing variables, “but if the product’s ultimate application subjects it to cyclic loading or temperatures, the fastening mechanisms could introduce a failure mode not present on a one-piece design.”
Ann, I assume your statement regarding aluminum or steel in the first paragraph is incorrect considering the text of the rest of the article. It is an interesting one, by the way. Recently there was an article on this site on Metal Injection Molding (MIM), which had a poor reputaiton, but has seen great improvements.
One observation is about the statement about increased pressure on manufacturing. This is a common statement, so my comment is not aimed at your article, particularly. There would be no increased pressure without advances in science and engineering. The statemnt seems to imply that these industries are standing still and being pushed by someone else. In reality US industry is among, if not the most , efficient in the world.
Another interesting point in your article is about the Scientific Molding process. I once worked for a company that made simulators, primarily for training. These included flight, military as well as industrial simulators. In general, the simulators were very accurate. They could often be driven faster than real-time. A secondard market was found for the industrial simulators in plant control. The simulator could run many scenarios with different feed stocks, etc. This would allow adjustment to the process before acutally consuming anything.
Finally, your article points out the need for design for manufacturing. Before the move toward outsourcing, there was a move toward integration. If you could design a part to be more easily manufactured, and you did it in the design phase, it was a very inexpensive change. If this had to be addressed later, it would be very costly. Perhaps we are moving back.
I heard an example of this recently. A manufacturer of space heaters, I think it was, brought their manufacturing back to the US. By a small redesign, one that eliminated a lot of fasteners, they were able to lower the time to manufacture. Since their market was mostly here, and since they could make changes to respond to market conditions more quickly, they have improved their competitiveness. A god example, I think.
How else can you design a part to be manufactured without understanding the capabilities and limitations of the manufacturing process? Evidently it has been done, but it doesn't make sense. It seems that others have thought differently over the years, which is probably the basis for the whole "DFM" group of consultants who try to solve problems for those designing hard to manufacture parts.
Injection molding has been one of those areas where the first step of part design has been to determine the capabilities needed to produce the part features while designing those same features. That would determine which supplier was selected as well as what features of the part could be included. An analogy is deciding what one would ,ake for dinner based on what food was on hand and what was available to cook it with.
Theoption of including secondary operation types of actions while the part is molded is quite interesting, and it would allow a number of additional options for the initial design process.
NEWS FLASH!!! We had better hope the Chinese don't get wind of this. They'll be flooding us with useless injection molded things for us to play with instead of actually working.
Our land fills will begin filling up with plastic toys, pc keyboards, mice (the electronic ones), cups, dishes, dinnerware, car instrument panels, you get the idea.
I don't make any claim of originality about the assertions in my previous posting, nor that the concepts presented are that new. In fact, my intended point was "how else could you do it? The idea of keepingproduction isolated from design and engineering has always been a poor choice. At least, I think that we are all aware that it is a poor choice.
I agree with William--when I first heard of DFM, my initial reaction was--"as opposed to what? Design Not For Manufacturing? Design Without Manufacturing?" DFT made sense, and later, DFR (R = either reassembly or recycling). OTOH, manufacturing processes, especially on highly automated lines, have gotten highly complex, as have some products, so more tailored DFM makes sense.
As long as injection molding has been around, it's good to hear about advances in this "old" technology to improve its performance. Sometimes what's needed is an evolution, not a revolution.
William, I think the analogy you used is apt, and I definitely welcome the prevalence of idea that good design is by definition design for manufacture, but that precludes the fact that there are so many poorly designed products in the marketplace. How many times have you seen an injection moulded product with significant sinking? or another with a level of fabrication that clearly could be vastly simplified with snapfits?
So, to take your analogy a little bit further, if you were making a meal out of the ingredients in your cupboard, and you were intending to create a curry, but only had salt, pepper, tumeric, milk and chicken, you would do the best you could with the ingredients that matched the recipe. But what if you had other ingredients that don't normally feature in a curry, like bicarbonate of soda, or vinegar, or butter? They aren't on the list, so you overlook how they could be used in your best-effort "design". If you had the time and inclination, you could research how these other ingredients could produce much more vibrant flavour combinations and thus produce a better assimilation of the real thing.
But that still isn't really analogous of the DFM issue, To be a proper analogy, not only would the ingredients have to be throughly explored for suitability, the cooking of the dinner would have to be streamlined for bulk output, so you'd figure out your prep times, brebatch certain ingredients, cook everything in one pot instead of four, and steam your rice in a double boiler over the top. These are all simple efficiency tweaks, and it is merely another form of tweak that brings the concern for efficiency into the design process instead of the re-design process where mistakes and time wasted are corrected after the fact or through manufacturing hacks on the production line.
If you are a good designer, are you already implementing DFM? Well most likely yes, but it is possible that you aren't and the DFM takes place at the design checking stage, where people with more experience of manufacturing provide their input, but if you are a bad designer, then you definitely aren't taking any consideration of the manufacturing process (or at least as little as is necessary to develop a product) and that means a lot of wasted time, money, resources and ultimately really poor, crappy products that are nothing more than future landfill.
jrryan , an interesting comparison to cooking. But if I don't have the ingredients for curry, then instead of making a deffective curry I would head in another direction and possibly make some fried chicken or beef stew.
My point is that unless one is intendingg to lead the organization in a new direction, it is a requirement to consider the production capabilities during the design stage, long before checking happens. Not only considering processes available, but also accuracy levels and the cost of those accuracy levels. Ultimately it equates to designing for high yield, hopefully 100%. That can only happen if one keeps production in mind at all times.
As for some of those poorly done injection molded parts with sink marks? YES, I have seen a few of them, and mostly the sink marks are in places where appearance does not matter much. I agree that sink marks are a production flaw, but sometimes they don't affect yield.
Of course, it is not certain that every engineer would also understand the ability of their organizations production department, but it is certain that at least some part of a design team should have a good grasp of how the product would be made. For many years I have asked other engineers, as we were discussing a design, "How would they make that?", and on quite a few occasions the designer had to visit the production people and find out. I have saved companies a few dollars that way, on occasion. It turns out that there are a few things that can be designed but that can not be produced, at least, not economoically.
Well william, you are Designing For Manufacture already then. I can tell you, there are designers and even engineers who are not. At least not for efficient manufacture. And as the addage of many ways to skin a cat goes, There are many ways to design a product for the same manufacture process. Just because the manufacture dictates how it is designed, doesn't necessarily follow that that is the most efficient design for manufacture. How long does it take to fabricate for example, does it require as many screw? Does it require screws at all? Do the parts require turning over to fit together on the assembly line? If so can they be designed to reduce the amount of turns? Are there sufficient guides in place to ease fitting parts together? Does the design require a certain finish, if not, can it be sparked for easier.quicker removal from the mould? How many other products can we incorporate parts from one or more common moulds? Etc...
As you've already demonstrated with your own experience, this kind of thinking in the design phase is the way forwards for good design engineers, yet not everybody leaving university is leaving with this drummed into their heads.
Since most of my working in the more recent past has been for smaller companies, the motivation is much closer to home, since we need to get any product right the very first time, or else we don't make any profit on it. That is some real motivation, as you can imagine.
The use of Scientific Molding is a great way to produce repeatable parts on multiple machines. Documentation of separation of pack and hold as well as a documented gate seal study helps to produce parts consistently on different machines.
In regards to aluminum tooling, what is the effect of glass filled reins on the aluminum mold? Often times, it is necessary to use glass filled resins for metal replacement projects.
Interesting point on the improved mold performance using aluminum due to its improved thermal conductivity. Do you know what type of aluminum they used? (QC-7?)
Greg, no details were given on the specific aluminum grades used for tooling, but both Unique and DRS mention that it varies depending on volume and lifecycle constraints.
P.S. this link contains some interesting further reading on aluminium tooling for injection moulding: http://www.phoenixproto.com/about/aluminum-tooling-information/aluminum-tooling-myths/ as expected 7075 and QC-10 are in there, along with a few other variants.
The 100-percent solar-powered Solar Impulse plane flies on a piloted, cross-country flight this summer over the US as a prelude to the longer, round-the-world flight by its successor aircraft planned for 2015.
GE Aviation expects to chop off about 25 percent of the total 3D printing time of metallic production components for its LEAP Turbofan engine, using in-process inspection. That's pretty amazing, considering how slow additive manufacturing (AM) build times usually are.
A $1,500, hand-operated, bench-model, plastic injection machine crowdsource-funded via Kickstarter can be used to mold small, quality, plastic parts inexpensively, on demand.
The federal government is launching competitions to kickstart three more manufacturing innovation institutes, including one focused on Lightweight and Modern Metals Manufacturing Innovation.
The airframe of Airbus's A350 XWB consists of a bigger proportion of carbon-fiber-reinforced composite structures than any other commercial jet to date: over 53 percent by weight.
From Dell / Intel® New Paradigms in Design Work Scott Hamilton, vertical market strategist for Dell Precision workstations, 5/2/2013 5
Early in my career, I worked as a draftsman and remember the days of drawing on vellum with numbered pencils and Mylar with plastic lead. This was a fun experience in the sense that I ...
I've been using workstations for more than 10 years and love finding ways to get more performance from my system. With demanding professional applications that require more power each ...
A lasting memory from my first job as an engineer in an auto assembly plant is standing on hard concrete at six in the morning, vending-machine coffee clutched in hand, listening to ...
For industrial control applications, or even a simple assembly line, that machine can go almost 24/7 without a break. But what happens when the task is a little more complex? That’s where the “smart” machine would come in. The smart machine is one that has some simple (or complex in some cases) processing capability to be able to adapt to changing conditions. Such machines are suited for a host of applications, including automotive, aerospace, defense, medical, computers and electronics, telecommunications, consumer goods, and so on. This radio show will show what’s possible with smart machines, and what tradeoffs need to be made to implement such a solution.
To save this item to your list of favorite Design News content so you can find it later in your Profile page, click the "Save It" button next to the item.
If you found this interesting or useful, please use the links to the services below to share it with other readers. You will need a free account with each service to share an item via that service.
Tweet This
16 